RAYSTON SPRAY FOAM 40 - Spain
RAYSTON SPRAY FOAM 40 - Spain
DESCRIPTI ON and APPLICATIONS
Rayston SPRAY Foam has been designed for a spray rigid polyurethane foam for thermal insulation in construction applications, with an applied density of 50 - 60 Kg/m3. The blowing agent in the polyol formulation is a HFC. Resulting foams are combustion modified according the norm ISO 3582
1. Numerical flame spread or fire classification are only indicative, they are not sales specifications and they are obtained from tests in our laboratories.
2. Numerical flame spread or fire classification are not intended to reflect hazards presented by this or any other material under actual fire conditions
GỌI NGAY 0913 404 017 - 0985 406 777 ĐỂ ĐƯỢC TƯ VẤN
PU Foam insulation sprayed Video for cold storage
PRODUCT DATA
Recommended Process Conditions
Typical reaction
Characteristics (1)
|
Units |
Polyol |
Isocyanate |
Test Method |
|
|
Hydroxyl Nr |
mg KOH/g |
267 |
ASTM D 4274d |
|
|
NCO content |
31% |
ASTM D 5155 |
||
|
Viscosity |
mPa.s |
350 (at 20/20ºC) |
ASTM D 4878 |
|
|
Viscosity |
mPa.s |
210 (at 25/25ºC) |
ASTM D 4889 |
|
|
Specific Gravity |
1.14 (a 20/20ºC) |
1.23 (a 25/25ºC) |
ASTM D 891 |
To be used in machines with volumetric relation 100:100.
|
Units |
Values |
||
|
Polyol |
by volume |
100 |
|
|
Isocyanate |
by volume |
100 |
|
Units |
Hand Mixing |
Method |
||
|
Cream Time |
s |
1 |
- 4 |
Internal Krypton Method |
|
Gel Time |
s |
5 |
- 14 |
Internal Krypton Method |
|
Rise Time |
s |
12 - 20 |
Internal Krypton Method |
|
|
Free rise density |
42 - 50 |
Internal Krypton Method |
||
1. Data refer to laboratory tests made with components at 20°C, hand-mixed with mechanical stirrer at 3000 rpm.