Pure Polyurea QP350-E


The 100% pure polyurea  QP350-E is a two component, solvent free, pure poly-urea of high reactivity, hot applied spray, suitable for waterproofing and protection of concrete.

GỌI NGAY 0913 404 017 - 0985 406 777 ĐỂ ĐƯỢC TƯ VẤN

Once applied, it provides a high performance continuous elastomeric membrane for waterproofing of roofs, terraces, bridge decks, underground structures, etc.

APPLICATION FIELDS

Waterproofing and protection of all types of roofs, green roofs, terraces, balconies, etc. Waterproofing of bridge decks, parking decks, etc.
Protection of polyurethane foam insulation. Waterproofing of channels, reservoirs, wastewater treatment plants and other water retaining structures, etc.
Protective coating on drainage boxes, retaining tanks or areas exposed to spillages and spattering of chemical compounds


ADVANTAGES

Forms a seamless continuous membrane.
Very good chemical resistance to water, seawater, wastewater, fuels, grease and oils, de-icing salts, diluted alkali and acid solutions, etc.
Very good elasticity, tear strength and abrasion resistance. High yields by spraying means.

TECHNICAL DATA

CuredFilmProperties


Test Method


TypicalValue


Solidscontent

 


100%


ShoreD hardness


ASTM D2240


45 (±5)

 
Elongation

 


ASTM D412


300%


Tensilestrength at break (MPa)


UNE-EN ISO 527-3


15(±2)


Tearstrength (N/mm)


DIN 53 5115


60(±2)


Moisturevapor transmission


ASTM E-96


0.02 perm


Abrasionresistance,weight loss


ASTM D4060


150 - 250mg

 
Gel time

 


10seconds
 


Tackfree

 


15seconds


Adhison strength on concrete surface


ASTM D4541


1.2Mpa


Water Absorption


ASTM D570-81


0.5%


Water Vapour Transmission


ASTM E96-80 at 230C


3.3g/m2 /day


Chemical resistant:

- Anti-frost (etylen glycol)

- Calcium chloride

- Diesel

- Gas

- Diesel Oil

- Sodium chloride


ASTM D543


None

None

None

None

None

None


Electricity Resistant:

- Volume

- Surface


ASTM D257

(Test voltage 500V)


4.3x1012 ohm inches

9.2 x 1013 ohms


Resistance tofreezing/frozendischarge

Ion Clorua penetration(%)


BD47 B4.2(f)
MaximumTolerance 0.04%


Passed
0.00%


Static crack Bridging

UK Department of Transport:

Technical Memorandum BE27: appendix B


2mm at 20OC


Heat aging

BS903:A2:1995 (ISO:1994)

Undertaken at 700C for 1 year

Tensile strength

Elongation at break

No significant change

No significant change


Heat agingresistance


BD47 B4.2(g)


Passed


Chloride Ion penetration (%)


MaximumTolerance  0.04%


0.00%


Againstchisel impact

Chloride Ion penetration(%)

At   – 10ºC

At   – 23ºC

At   – 40ºC
 


BD47 B4.2(h)

MaximumTolerance  0.04%

MaximumTolerance  0.04%

MaximumTolerance  0.04%

Passed

0.00%

0.00%

0.00%


Against aggregate indentation – Chloride Ion penetration(%)

At   40ºC

At   80ºC

At  125ºC
 


BD47 B4.2(I)

MaximumTolerance  0.04%

MaximumTolerance  0.04%

MaximumTolerance  0.04%


Passed

0.00%

0.00%

0.00%


Cyclethermal shockthermalcrackingandaging – Chloride Ion penetration (%)

At   – 10ºC

At     23ºC

At     40ºC
 


BD47 B4.2(j)

MaximumTolerance  0.04%

MaximumTolerance  0.04%

MaximumTolerance  0.04%


Passed

0.00%

0.00%

0.00%

Spraying on the concrete surface treated by crystal line capillary waterproofing penetration sealer

 

No interactive

Metal drums of 225 kg each component(amines and isocyanates)